Dekalin DEKAsyl MS 5 sylil modified polymer power glue 290 mL (black)

DEKAsyl MS-5 is a high-quality power adhesive with a high initial strength which can be used in all areas of vehicle construction.
The areas of use and application are diverse and can be extended as required.

Colour: Black
Content: 290 ml
Packaging: Cartridge

Areas of application:

Bonding of, among others:

- Metal frames
- Corner profiles
- Structural bonding of polyester parts
- Climate boxes
- solar systems
- SAT systems
- Frames and wheel covers
- and much more

Proper application:

DEKAsyl MS-5 can be easily applied with a hand or air pressure gun. For sealing, Dekasyl MS-5 should be applied within 12 minutes (at 20°C/50 % rel. humidity) with a cloth previously dipped in a mild soap solution.
Dekasyl MS-5 should be further processed or smoothed with a spatula or putty knife previously dipped in a mild soap solution.
Avoid penetration of the side solution between the joint sides and the sealant, as this leads to a loss of adhesion.
this leads to a loss of adhesive strength. For bonding, the substrates must be dried within 15 minutes (at
20°C/50% rel. humidity) after application of Dekasyl MS-5. The higher the temperature
the shorter the processing time! In general, an adhesive layer of 2 mm is recommended if similar materials
materials (with similar strength) are to be bonded. The greater the difference in thermal expansion, the thicker the adhesive layer should be. At a temperature of 20°C and a relative humidity of 50%, Dekasyl MS-5 can be applied with most industrial paints after just 10 minutes.
can be painted over with most industrial paints after just 10 minutes. The best possible adhesion of
The best possible adhesion of colour layers is achieved when the paint is applied 4 hours after application of Dekasyl MS-5. Clean the tools or remove uncured residues of Dekasyl MS-5 with a clean, colourless cloth soaked in acetone or MEK (it is recommended to check beforehand whether the surface is attacked by this cleaner).
surface is attacked by this cleaner).

Technical data:

Base material: MS Polymer
Curing/sealing: Moisture

Specific density: approx. 1.4 kg/litre
Skin formation time (20°C/50% rel. LF): approx. 12 minutes

Open time (20°C/50% rel. LF): < 15 minutes
Curing after 24 h (20°C/50% rel. LH): approx. 4 mm

Shore A hardness (DIN 53505): approx. 55
Volume change (DIN 52451): < 3%

Adhesive strength (physical rheometer MC100): approx. 700 Pa
(measure of the maximum uncured adhesive quantity that can be applied per m² without running down)

Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 MPa
Tensile stress at break (DIN 53504/ISO 37): approx. 2.8 MPa

Elongation at break (DIN 53504/ISO 27): approx. 210%
Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa

Tear strength (DIN 53515/ISO 34): approx. 14 N/mm
Solvent content:0%

Isocyanate content:0%
Temperature resistance: -40°C to +120°C