DEKAsyl MS-2 is the ideal compromise between adhesive and sealant for the production of elastic connections between components, which additionally require a high adhesive strength.
DEKAsyl MS-2 glues and seals in one and does not weaken the installed material and leaves no traces of joining elements (screws or similar).
Overpainting of the MS-2 adhesive sealant is possible after skin formation.
The areas of use and application are diverse and can be extended as desired.
Colour: Grey/Black/White
Content: 290 ml
Packaging: cartridge
Fields of application:
- Aluminium
- polyester
- GRP
- PMMA
- Compensation of construction tolerances
- glass
- Roof hatches and windows
- wheel coverings
- and much more
Base material: MS Polymer
Curing/sealing: Moisture
Specific density: approx. 1.4 kg/litre
Skin formation time (20°C/50% rel. LH): approx. 10 minutes
Open time (20°C/50% rel. LF): < 15 minutes
Curing after 24 h (20°C/50% rel. LH): approx. 3 mm
Shore A hardness (DIN 53505): approx. 55
Volume change (DIN 52451): < 3%
Adhesive strength (physical rheometer MC100): approx. 300 Pa
(measure of the maximum uncured adhesive quantity that can be applied per m² without running down)
Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 MPa
Tensile stress at break (DIN 53504/ISO 37): approx. 2.6 MPa
Elongation at break (DIN 53504/ISO 27): approx. 250%
Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa
Tear strength (DIN 53515/ISO 34): approx. 16 N/mm
Solvent content:0%
Isocyanate content:0%
Temperature resistance: -40°C to +120°C
Application temperature: +5°C to +35°C
UV and weather resistance: excellent